Create a slurry using CMC-Li, created an electric double layer capacitor using aluminum as an electrode that the slurry was applied.

The characteristics of the slurry,the viscosity strongly and easily coated. even after drying, unevenness don't mentioned.

Battery-powered

Al||CMC-Li,SBR,CNT|5wt%AAaq|SuS

Coating amount of CMC-Li was 0.0118 g and Carbon content was 4.37 mg

Capacitance per CNT 1mg was 129 ƒÊF/mg

measured CV, the capacitance of the anode side first week was 0.57 mF and second week also 0.57 mF was observed.

Large reduction in the also capacitance didn't observed.

Consideration

Features of the CMC is small reduction of the capacitance but inferior in size of the capacitance as compared to the others.